Care and maintenance of metallic equipment

Posted by BMC on 03/03/2002

Life moves fast these days. With the increasing popularity of climbing, manufacturers are taking every advantage of the latest advances in materials and technology to make exciting new gear available each year.

But one thing never changes, climbing has been and always will be a risk sport, and all the latest equipment in the world will only increase the margin of safety at which you operate. Risk can never be eliminated, so it’s absolutely vital to understand the limitations of equipment, and recognise the situations that may cause it to become damaged or even fail.

But how do you know if a certain piece of equipment is damaged? Should you throw a rope away after washing it in detergent? What’s a stress fracture? That’s where the long anticipated new edition of the BMC’s Care & Maintenance Book comes in. This is a concise 60 page full colour guide to caring for your kit, and should be one piece of equipment not to forget. Just one of the important subjects covered is degradation of metallic equipment, so read on if even if you only own a single karabiner, and especially if you’ve ever dropped it in the sea!

Equipment degradation
Every time you use your gear it is under attack from a variety of sources - UV light, dirt, dust, water, salt – really, the surprise is not that climbing gear sometimes fails, but that it doesn’t more often! Here are some of the more common forms of metallic degradation that occur, and some of the ways in which you can combat them:

Seawater corrosion
Seawater and airborne sea spray present a number of corrosion problems of varying severity to all metallic climbing equipment. In all cases the corrosive agent is aqueous chloride ions from the salt in the water, and this generally attacks moving parts such as the gate, springs and latch, or areas of equipment where two different alloys are in contact with each other.

After every use of climbing gear on sea cliffs, and anywhere within the region of sea spray (which may extend well over and around the actual sea cliff in rough weather), it is recommended that the following procedure be carried out:

After finishing climbing for the day - keep the dry gear separate from the wet, and make sure it is kept away from any damp ropes, slings and clothing etc – even to the point of carrying a drybag to store dry equipment. Any wet equipment should be washed thoroughly in tap water or a freshwater stream to remove all traces of salt, then after removal of surface water it should be hung out to dry. This should be done even if the plan is to climb again the following day.

If you are travelling home - do not leave any metal equipment that may be contaminated with salt in a rucksack or other carry bag where it may come into contact with slings or ropes – especially in a warm environment - as this will induce corrosion. If karabiners or camming devices are left like this for, say, a week, they will at the very least become discoloured and suffer surface corrosion. Within a few weeks, they could be so badly affected as to be unfit for further use – a costly mistake!

As soon as possible after returning home - all equipment that has been contaminated with salt water should be thoroughly washed in tap water, preferably with a little mild detergent. Then remove all surface water and put in a warm, dry airy place (such as a rack in an airing cupboard) to dry off the remaining moisture. With chocks and camming devices, take special care that the wire cables have been thoroughly washed and dried.

When dry - any hinges, movable joints, wires & cables etc. should be treated with a suitable aerosol lubricant, any surplus wiped away, and the movement checked before storage.

Fatigue
Whilst the maximum failure load is a concept central to all engineering applications and their designs, another aspect of equal concern is fatigue. Fatigue is well recognised by professional engineers in nearly all materials, but especially in metallic alloys since it affects the life span of a product. If a load is applied that is lower than the stipulated failure load of a particular piece of equipment, but is done so repeatedly, then the piece may eventually fail. This process is known as fatigue failure. Each load application is known as a cycle, and the less the load, the more cycles are required to cause a failure (if the load is small enough then a failure will never happen) However in reality for climbing equipment, the load level over a sequence of cycles is not constant, and a sudden big load equalling the failure load will cause the piece to fail.

The importance of fatigue effects implies the need to keep the amount of load to a reasonable level- well below the failure load- and to avoid sudden large loads, thus prolonging the fatigue life of the item. The design of a piece of equipment should take fatigue into account in the following way:

“The usual loads expected should be such that many thousands of cycles are required before fatigue failure, and this should be beyond the expected usable lifetime of the product”

However, if through exceptionally heavy or abnormal use too many cycles have been accumulated and failure is near, then cracks in the highest stressed areas will be forming and growing. Hence, a close examination with a magnifying glass on well-used equipment will be very worthwhile – a common example is cracking at the base of the front points of well-used crampons. In climbing terms, this means that reasonable use should attempt to avoid any chance of fatigue failure by limiting the number and/or severity of the load cycles. Examples of use that go against this are excessive torquing, or repeated hitting of hidden rocks under ice or hard, awkward walking over rocks in crampons. Both secnarios will shorten the useful life of the equipment involved

Wear
Wear is a phenomenon that occurs when metallic surfaces are rubbed by other surfaces under pressure, and local shear stresses arise. Because of these, particles on the surface are eroded, and the physical volume of material locally decreases. The higher the contact pressure and the softer the material, the greater the rate of wear will be. Sharp surface features (like edges and corners) will also erode quicker than smoother parts, because the stresses in those features are higher under a rubbing force. For climbing equipment, any contacting surfaces are liable to wear since most alloys in common use are relatively soft. The most usual high-pressure situation encountered in practice is that of ropes passing through karabiners, abseiling and belay devices etc. Grooves can appear in these items of metallic equipment, and since a noticeable groove represents a new surface geometry with some material removed, the performance of these items will alter over time. This has the further implication that the failure load and other design parameters of the item are changed, and a safe course of action is to retire the piece of equipment once such a groove has become noticeable.

Stress degradation
Any piece of equipment that operates under applied loads becomes subject to the effects of the stresses that result from those loads. Thus, any structure or component used in an engineering application becomes stressed during the normal course of their intended operation, and metallic climbing equipment is no exception to this.
For instance, when a climber falls, the rope takes the climbers weight along with the harness, karabiners, slings and protection placed – all become stressed to a degree. The manufacturers design their equipment to withstand these stresses, but in conjunction with wear & tear and time, continued stressing sometimes leads to a failure. For example (again!), crampon points and ice tools are subjected to continual and sometimes abnormal loading (as in torquing when mixed climbing), which can sometimes be above and beyond the intended design load. In some cases, this load is greater than the equipment can sustain and failure results.

Cracking
The presence of cracks in any structure that is designed to carry load is potentially dangerous, but obviously so where metallic climbing equipment is involved. Cracks can arise for several reasons:

During manufacture or heat-treatment of the equipment, commonly during welding processes – these are invariably detected at an early stage, or not critical to the intended performance of the equipment.

During a sudden overload when the failure load is exceeded and the item breaks – this is effectively the sudden initiation and catastrophic growth of a crack through the weakest part of the equipment.

Due to corrosion.

By fatigue - as previously explained. Such a crack starts at a microscopically small size, growing as the fatigue life progresses until it is big enough to be noticed by the naked eye. In climbing equipment, this usually means that the fatigue life is nearly at an end, and that a failure is imminent. This is the reason for recommending regular inspections of equipment both with the naked eye and with a magnifying glass, and when such a crack is detected to retire the item immediately. Continued use of a cracked item will almost certainly lead rapidly to sudden failure – a very dangerous situation.

Another relevant consideration when considering cracks is the influence of temperature. If the temperature is low enough, the brittleness of a material can increase significantly and any small cracks are liable to sudden and catastrophic breaking, like shattering glass. At higher temperatures, materials exhibit a more ductile characteristic making sudden cracking much less likely. For the alloys used in climbing equipment, the transition temperature between this brittle and ductile behaviour occurs somewhere in the range -50ºC to +50ºC.
The important factor for climbing equipment is that at cold extremes, it is more liable to brittle fracture, and prolonged use in these conditions increases the likelihood of this occurring (eg. during an expedition). Although a lot of care is taken to consider this during design and material choice, it is prudent to check regularly for cracks in equipment that is used at cold temperatures for extended periods of time.

For further information on advice on how to look after all your gear, consult the new edition of Care & Maintenance.


As Europe is unlocked, BMC travel insurance is loaded with the essential cover that you need for adventure.  

From 10 July, many European destinations are opening up to UK travellers. This means that you can still have your summer adventure – from sport climbing in Spain to trekking in the Alps.

BMC travel insurance comes in five policies: Travel, Trek, Rock, Alpine and Ski and High Altitude.

All of our policies include the following Coronavirus cover:

  • 24-hour emergency assistance helpline
  • £10 million emergency medical cover
  • £100,000 Search, rescue and recovery cover

Please be aware that there is no cover for cancellation, curtailment, delays or journey disruption in any way caused by or resulting from coronavirus / Covid-19. Read more about the Covid-travel FAQs here


« Back

Post a comment Print this article

This article has been read 2090 times

TAGS

Click on the tags to explore more

RELATED ARTICLES

Caring for your equipment
0
Caring for your equipment

Do you know when to retire your climbing gear? Can you decide if any damage is dangerous or just cosmetic? Keep safe when climbing by making sure your equipment is up to the job, with the help of advice guides and videos from the BMC.
Read more »

Behind the scenes: equipment
1
Behind the scenes: equipment

Continuing our series of articles about the work of volunteer-led BMC specialist committees, we highlight the work of the Technical Committee, which works with manufacturers and other partners to provide unbiased advice on safety equipment for climbing and mountaineering.
Read more »

Safety alert for Fixe lower-offs: updated
1
Safety alert for Fixe lower-offs: updated

The DAV (German Alpine Club) have issued a safety alert for lower-off units from manufacturer Fixe, some of which have been reported to fail by cracking of one of the chain links. These units are primarily designed for use at indoor walls, but are also sometimes installed outside with the hangers mounted onto expansion bolts to provide an outdoor lower-off.
Read more »

Post a Comment

Posting as Anonymous Community Standards
3000 characters remaining
Submit
Your comment has been posted below, click here to view it
Comments are currently on | Turn off comments
0

There are currently no comments, why not add your own?

RELATED ARTICLES

Caring for your equipment
0

Do you know when to retire your climbing gear? Can you decide if any damage is dangerous or just cosmetic? Keep safe when climbing by making sure your equipment is up to the job, with the help of advice guides and videos from the BMC.
Read more »

Behind the scenes: equipment
1

Continuing our series of articles about the work of volunteer-led BMC specialist committees, we highlight the work of the Technical Committee, which works with manufacturers and other partners to provide unbiased advice on safety equipment for climbing and mountaineering.
Read more »

Safety alert for Fixe lower-offs: updated
1

The DAV (German Alpine Club) have issued a safety alert for lower-off units from manufacturer Fixe, some of which have been reported to fail by cracking of one of the chain links. These units are primarily designed for use at indoor walls, but are also sometimes installed outside with the hangers mounted onto expansion bolts to provide an outdoor lower-off.
Read more »

BMC MEMBERSHIP
Join 82,000 BMC members and support British climbing, walking and mountaineering. Membership only £16.97.
Read more »
BMC SHOP
Great range of guidebooks, DVDs, books, calendars and maps.
All with discounts for members.
Read more »
TRAVEL INSURANCE
Get covered with BMC Insurance. Our five policies take you from the beach to Everest.
Read more »